Publication Date 02.02.2017
Applicants HEBEI CHENYANG INDUSTRY & TRADE GROUP CO.,LTD
Pub. No WO/2017/016091

Abstract

Disclosed are an interior wall water paint for a children’s bedroom and a preparation method therefor. The water paint is prepared according to the following proportion of raw materials by weight percentage: 25-50% of an anionic odor absorber styrene-acrylic emulsion, 5-10% of an organic siloxane modified polymer emulsion, 0.05-0.1% of a pH regulator, 14-30% of deionized water, 0.1-0.4% of a wetting agent, 0.1-0.5% of a freeze-thaw resistant stabilizer, 0.1-0.5% of a defoaming agent, 0.4-0.8% of a dispersing agent, 0.2-0.4% of a preservative, 0.1-0.3% of a film-forming assistant, 0.5-1% of a thickener, 0.3-0.8% of a leveling agent, 20-25% of titanium pigment, 3-5% of anti-formaldehyde powder, 1-3% of a matting powder and 5-15% of ground calcium carbonate.

Claims

The claims are defined in the claims.

The invention relates to an interior wall water paint for a child room the interior wall water paint is characterized in that the interior wall water paint is characterized by comprising an interior wall water paint for a child room, according to the weight percentage, the material is prepared from the following raw materials in percentage by weight:

Emulsion: 25 -50% anionic net flavor styrene-acrylic emulsion and…. 5 -10% Of an organosiloxane modified polymer emulsion; and c, modifying the polymer emulsion by using an organosiloxane modified polymer emulsion of 5 -10%; and

The auxiliary agent comprises 0.05 -0.1% of pH-adjusting diij and 14 -30% of deionized water, 0.1 -0.4% of tpii, 0.1 -0.5% of anti-freeze-thaw stabilizer, 0.1 -0.5% of anti-freeze-thaw stabilizer, 0.1 -0.5% of anti-freeze-thaw stabilizer, 0.1 -0.5% of anti-freeze-thaw stabilizer, 0.1 -0.5% of anti-freeze-thaw stabilizer, 0.1 -0.5%, 0.1 -0.5% of a defoaming agent, 0.4 -0.8% of a dispersing agent, 0.2 -0.4% of a preservative, 0.2 -0.4% of a preservative, 0.2 -0.4% of a preservative and 0.2 -0.4% of a preservative, 0.1 -0.3% of a coalescing agent, 0.5 -1% of a thickener, 0.3 -0.8% of a 0.3 -0.8% of a thickener, 0.3 -0.8% of a thickener, 0.3 -0.8% of a thickener, 0.3 -0.8% of a thickener, 0.3 -0.8% of a thickener, 0.3 -0.8% of a thickener, 0.3 -0.8% of

Lltcc; a leveling agent of the lacht; and a leveling agent of the lacht; and a flatting agent of the

20 -25% Of titanium dioxide, 3 -5% of anti-formate powder, 20 -25% of titanium dioxide, 3 -5% of anti-formate powder, 20 -25% of titanium dioxide, 3 -5% of anti-formate powder, 1 -3% of matting powder, 5 -15 parts of extinction powder and 5 -15 parts of extinction powder,

% Of heavy calcium carbonate; and uniformly stirring

The interior wall paint for child room according to claim 1, as claimed in claim 1., the anti-freeze-thaw stabilizer is an anti-freeze-thaw stabilizer with the boiling point of more than 400°c the anti-freeze-thaw stabilizer is characterized in that the anti-freeze-thaw stabilizer is an anti-freeze-thaw stabilizer with the boiling point of more than 400° c.

The interior wall paint for child room according to claim 1, as claimed in claim 1., the invention is characterized in that the extinction powder is a synthetic aluminum silicate functional filler with a hole structure

The inner wall paint for child room according to claim 3, as claimed in claim 3, it is characterized in that the extinction powder is zeoleo 330 of US pat. inc. zoleak 330,

The inner wall paint for child room according to claim 1, as claimed in claim 1., the anti-formaldehyde powder is characterized in that the formaldehyde-resistant powder is a TK 401 of shanghai shandong chemical technology co. inc. inc. inc. inc.

The inner wall paint for child room according to claim 1, as claimed in claim 1., the thickening agent is characterized in that the thickening agent is hydroxyethyl cellulose and hydroxyethyl cellulose, anionic alkali swelling thickener and polyurethane thickener

The interior wall paint for child room according to claim 1, as claimed in claim 1., the defoaming agent is characterized in that the defoaming agent is a mineral oil defoaming agent and a molecular-level defoaming agent, the weight ratio of the mineral oil defoaming agent to the molecular-grade defoaming agent is 1: 3

The interior wall water paint for child room according to claim 1, as claimed in claim 1., the rutile type titanium dioxide is characterized in that the titanium dioxide is rutile type titanium dioxide; the wetting agent is a non-ionic type environment-friendly wetting agent which does not contain alpha [ rho [ epsilon ], and is an environment-friendly wetting agent

The invention provides a method for manufacturing an interior wall paint for a child room according to any one of claims 1 -8. The interior wall paint for the child room comprises any one of claims 1 -8, the method is characterized by comprising the following steps:

The method comprises the following steps: adding the deionized water of which the ratio is four to four into the paint mixing tank according to the formula amount, and stirring to obtain the deionized water; sequentially adding one third of the thickening agent, the pH regulator and the pH regulator into one third of the thickening agent and the pH regulator, a wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a defoaming agent; and preparing the wetting agent, the anti-freeze-thawing stabilizer, the dispersing agent and the defoaming agent

Step b, stirring, sequentially adding the titanium dioxide powder and the titanium dioxide powder according to the formula amount, and sequentially adding the titanium dioxide powder, the titanium dioxide powder and the titanium dioxide powder according to the formula amount, anti-formaldehyde powder, matting powder and heavy calcium; and the anti-formaldehyde powder, the matting powder and the heavy calcium; and

Step c, stirring, pulping the paint pulp, wherein the fineness of the paint pulp is less than or equal to 55 micrometers; step d, stirring, wherein the fineness of the paint pulp is less than or equal to 55 micrometers; step d, stirring, sequentially adding one-fifth of deionized water and a defoaming agent according to the formula amount, and sequentially adding one-fifth of deionized water and a defoaming agent; sequentially adding one-fifth of deionized water and a defoaming agent,

, An anionic odorless styrene-acrylic emulsion, an organosiloxane modified polymer emulsion, a coalescing agent, a preservative, a coalescing agent, a preservative, a coalescing agent and a preservative, the flatting agent and the third of the thickening agent with a viscosity of 25°c and the viscosity of 25°c are adjusted to be 25° c.

105 − 110 KU

The invention provides a method for manufacturing interior wall water paint for a child room according to claim 9, the method is characterized by comprising the following steps:

The method comprises the following steps: adding four parts of deionized water into the paint mixing tank according to the formula amount, and adding four parts of deionized water into the paint mixing tank according to the formula amount, stirring at a rotating speed of 300 -600 r/min to obtain a rotating speed of 300 -600 r/min., one third of the thickening agent, the pH regulator, the wetting agent and the wetting agent are sequentially added into one third of the thickening agent, the pH regulator and the wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a mineral oil defoaming agent; and the anti-freeze-thawing stabilizer, the dispersing agent and the mineral oil defoaming agent

Step b, adjusting the high-speed rotation speed to 600 -1000 r/min, and according to the formula amount, adding the high-rotation speed to 600 -1000 r/min, sequentially adding the titanium dioxide powder, the formaldehyde-resistant powder, the matting powder and the heavy calcium; and preparing the titanium dioxide powder, the anti-formaldehyde powder, the matting powder and the heavy calcium; and

Step c, increase the rotation speed to 1200 r/min, and increase the rotation speed to 1200 r/min., pulping the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers; and preparing the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers;

Step d, reducing the rotating speed to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800, sequentially adding one-fifth of deionized water, a molecular-level defoaming agent and an anionic pure-flavor styrene-acrylic emulsion, organic siloxane modified polymer emulsion, coalescing agent, preservative and leveling agent, 3-thirds of the thickening agent with a viscosity of 25°c and a viscosity of 105 -110.

Description of related art

[0002] With the improvement of the human living level, people have higher and higher requirements on the health requirements in life, especially for children, not only has good performance, but also is healthy and environment-friendly, and is healthy and environment-friendly, and is healthy and environment-friendly.. Child rooms are the major life field of children, so that the children’s home decoration becomes the focus of people. The interior wall coating for the child room not only needs to be color-adjusted and stain-resistant, but also is stain-resistant, stain-resistant, stain-resistant, stain-resistant, stain-resistant, stain-resistant, no heavy metal or low VOC (volatile organic compounds) or APEO (polyethylene glycol-free) or APEO (polyethylene glycol-free)-free APEO (polyethylene glycol-free) or APEO. The existing interior wall coating for a child room has a plurality of odor-removing coatings easy to color, in addition, the formaldehyde-resistant coating is poor in formaldehyde-resistant effect and generally does not have the stain-resistant function.

Field of the invention

[0003] The invention aims to provide an interior wall water paint for a child room and a preparation method thereof. The interior wall water paint for the child room comprises an interior wall water paint for a child room and a production method thereof, the water paint does not contain heavy metals, is low in VOC (volatile organic compounds), does not contain alpha rho epsilon o, and has the easy color adjustment function., the formaldehyde-resistant and stain-resistant characteristics of the odor-free interior wall coating, the formaldehyde-resistant coating and the stain-resistant coating are combined to form the odor-free interior wall coating, the formaldehyde-resistant coating and the stain-resistant coating, the current situation that the single function of the inner wall coating is changed is changed, the construction is simple, convenient, healthy and environmentally friendly.

The solution of the problem is as follows:

Technical solutions

[0004] In order to solve the technical problem, the technical scheme adopted by the invention is as follows: the interior wall paint for the child room comprises an interior wall paint for children, according to the weight percentage, the material is prepared from the following raw materials in percentage by weight:

[0005] Emulsion: 25 -50% anionic net flavor styrene-acrylic emulsion and…. 5 -10% Of organosiloxane modified polymer emulsion

[0006] 0.05 -0.1% Of an auxiliary agent, 0.05 -0.1% of a rho eta regulator and 14 -30% of deionized water, 0.1 -0.4% of tacht; 0.1 -0.5% of wetting of the mixture; and 0.1 -0.5% of ltps; and the anti-freeze-thaw stabilizing agent is an anti-freeze-thaw stabilizer, and the anti-freeze-thaw stabilizing agent is an anti-freeze-thaw stabilizer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5%, 0.4 -0.8% of a dispersing agent, 0.2 -0.4% of a preservative, and 0.1 -0.3% of a film-forming assistant ij, 0.5 -1% of a thickening agent and 0.3 -0.8% of a flatting agent; and preparing a flatting agent by using 0.3 -0.8% of a flatting agent

[0007] 20 -25% Of pigment and filler, 20 -25% of titanium dioxide, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5%, 1 -3% of light-extinction powder and 5 -15% of heavy calcium carbonate; and uniformly stirring the raw materials

[0008] Preferably, the anti-freeze-thawing stabilizer is an anti-freeze-thaw stabilizer with a boiling point of greater than 400° c.

[0009] Preferably, the extinction powder is a synthetic aluminum silicate functional filler with a hole structure

[0010] Further preferably, the extinction powder is zeylleash 330 of US pat. inc. zeylleash 330, USA.

[0011] Preferably, the formaldehyde-resistant powder is TK 401 of shanghai shengshan chemical technology co. inc. ltd. ltd.

[0012] Preferably, the thickening agent is hydroxyethyl cellulose, and the thickening agent is hydroxyethyl cellulose, anionic alkali swelling thickener and polyurethane thickener

[0013] Further preferably, in the thickener, hydroxyethyl cellulose is an anionic alkali swelling thickener: the weight ratio of the polyurethane thickener is 2: 3: 1

[0014] Preferably, the defoaming agent is a mineral oil defoaming agent and a molecular-level defoaming agent, the weight ratio of the mineral oil defoaming agent to the molecular-grade defoaming agent is 1: 3

[0015] Preferably, the titanium dioxide is rutile type titanium dioxide or rutile type titanium dioxide; the wetting agent is a non-ionic type environment-friendly wetting agent which does not contain alpha [ rho [ epsilon ], and is an environment-friendly wetting agent

[0016] The invention relates to a method for manufacturing an interior wall paint for a child room the method comprises the following steps: a, preparing an interior wall paint for a child room, comprising the following steps:

[0017] The method comprises the following steps: adding the deionized water of which the ratio is four to four into the paint mixing tank according to the formula amount, and stirring to obtain the deionized water; sequentially adding one third of the thickening agent, the pH regulator and the pH regulator into one third of the thickening agent and the pH regulator, a wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a defoaming agent; and preparing the wetting agent, the anti-freeze-thawing stabilizer, the dispersing agent and the defoaming agent

[0018] Step b, stirring, sequentially adding the titanium dioxide powder, the anti-formaldehyde powder, the matting powder and the calcium carbonate powder according to the formula amount, wherein the titanium dioxide powder, the anti-formaldehyde powder, the matting powder and the calcium carbonate powder are sequentially added into the titanium dioxide powder, the anti-formaldehyde powder, the extinction powder and the calcium carbonate powder according to the; step c, stirring, pulping the paint slurry, wherein the fineness of the paint slurry is less than or equal to 55 micrometers; and step c, pulping the paint slurry, wherein the fineness of the paint slurry is less than or equal to 55 micrometers;

[0020] Step d, stirring, sequentially adding one fifth of deionized water and one fifth of deionized water according to the formula amount, defoaming agent, anionic odorless styrene-acrylic emulsion, organosiloxane modified polymer emulsion and organic siloxane modified polymer emulsion, a coalescing agent, a preservative, a flatting agent and three thirds of the thickening agent, the viscosity is adjusted to be 25°c and the viscosity of the alzheimer’s viscosity is 105 -110

[0021] Preferably, the manufacturing method of the interior wall paint for the child room comprises the following steps: a, preparing an interior wall paint for a child room, comprising the following steps:

[0022] The method comprises the following steps: adding four parts of deionized water into the paint mixing tank according to the formula amount, and adding four parts of deionized water into the paint mixing tank according to the formula amount, stirring at a rotating speed of 300 -600 r/min to obtain a rotating speed of 300 -600 r/min., one third of the thickening agent, the pH regulator, the wetting agent and the wetting agent are sequentially added into one third of the thickening agent, the pH regulator and the wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a mineral oil defoaming agent; and the anti-freeze-thawing stabilizer, the dispersing agent and the mineral oil defoaming agent

[0023] Step b, adjusting the high-speed rotation speed to 600 -1000 r/min, and according to the formula amount, adding the high-rotation speed to 600 -1000 r/min, sequentially adding the titanium dioxide powder, the formaldehyde-resistant powder, the matting powder and the heavy calcium; and preparing the titanium dioxide powder, the anti-formaldehyde powder, the matting powder and the heavy calcium; and

[0024] Step c, increase the rotation speed to 1200 r/min, and increase the rotation speed to 1200 r/min., pulping the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers; and preparing the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers;

[0025] Step d, reducing the rotating speed to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800, sequentially adding one-fifth of deionized water, a molecular-level defoaming agent and an anionic pure-flavor styrene-acrylic emulsion, organic siloxane modified polymer emulsion, coalescing agent, preservative and leveling agent, 3-thirds of the thickening agent with a viscosity of 25°c and a viscosity of 105 -110.

[0026] Apeo is an alkyl phenol polyoxyethylene ether compound for short, the non-ionic surfactant which is widely used at present is the main representative of non-ionic surfactants which are widely used widely. The potential harm of APEO to the environment has been widely studied and demonstrated. European countries have formulated regulations limit production and use apeo-based regulations to limit the production and use of apeo (alkylphenol ethoxylates). The Apeo can be summarized into the following four aspects in terms of ecological influence: toxicity and toxicity, the biological degradability, the environmental hormone and the harmful by-products are generated in the production process

[0027] Voc is the english abbreviation of volatile organic compounds and volatile organic compounds. VOC (volatile organic compounds) in ordinary meanings refers to volatile organic compounds and volatile organic compounds; however, the definition in the environment-friendly sense refers to an active class of volatile organic compounds.,

BACKGROUND OF THE INVENTION

[0028] The beneficial effects of the technical scheme are as follows:

[0029] (1) The interior wall water paint for the child room is free of heavy metals, low in VOC (volatile organic compounds), low in VOC (volatile organic compounds) and low in VOC (volatile organic compounds), the APEO does not contain APEO, and has the characteristics of easy color adjustment, formaldehyde resistance and stain resistance.; the odor-free interior wall coating, the formaldehyde-resistant coating and the stain-resistant coating are combined together to form the three kinds of materials, the current situation that the single function of the interior wall coating is changed is changed, the construction is simple and convenient, and the interior wall coating is healthy and environment-friendly; the construction is simple and convenient, and the interior wall coating is healthy and environmentally friendly;

[0030] In the present invention, the anionic odorless styrene-acrylic emulsion and the organosiloxane modified polymer emulsion are adopted, good hydrophobicity and scrubbing resistance are provided for a paint film, so that the paint film is not polluted by stains, and the paint film is not polluted by stains., even oily stains are polluted by the oily stains, the wet rag can be scrubbed clean; meanwhile, the wet rag can be scrubbed clean even if the wet rag is polluted by oily stains;

[0031] According to the freeze-thaw stabilizer disclosed by the invention, the anti-freeze-thaw stabilizer with the boiling point of more than 400°c is adopted, and the anti-freeze-thaw stabilizer with the boiling point of more than 400°c is, the low-temperature storage stability of the coating is improved, and the VOC in the coating is greatly reduced; the coating is greatly reduced in the VOC in the coating; the coating is greatly reduced in VOC in the coating; the coating is greatly reduced in

[0032] (4) According to the invention, the TK 401 made by shanghai shengshan chemical technology co. ltd. is adopted as the anti-formaldehyde powder, and the TK 401 is made as the anti-formaldehyde powder., the formaldehyde can be adsorbed and harmful substances such as formaldehyde can be decomposed in the same time; the formaldehyde can be decomposed in the same time; the formaldehyde and other harmful substances can be decomposed in the same time

[0033] (5) According to the invention, a synthetic aluminum silicate functional filler with a hole structure is adopted, 85-degree light measurement can be effectively eliminated, and the eye protection is protected., the hole structure of the filler has the function of adsorbing harmful substances such as formaldehyde and the like., the TK 401 is assisted by shanghai shengshan chemical technology co. ltd. to decompose harmful substances such as formaldehyde and the like, and the effect is remarkable.

The embodiment of the invention is as follows

[0034] In order to make the objectives, technical solutions and advantages of the present invention more comprehensible, technical solutions and advantages are clearer., the present invention will be further described in detail with reference to specific embodiments.

[0035] The invention relates to an interior wall paint for a child room, according to the weight percentage, the material is prepared from the following raw materials in percentage by weight:

[0036] Emulsion: 25 -50% anionic net flavor styrene-acrylic emulsion and…. 5 -10% Of organosiloxane modified polymer emulsion

[0037] 0.05 -0.1% Of a pH regulator and 14 -30% of deionized water, 0.1 -0.4% of tacht; 0.1 -0.5% of wetting of the mixture; and 0.1 -0.5% of ltps; and the anti-freeze-thaw stabilizing agent is an anti-freeze-thaw stabilizer, and the anti-freeze-thaw stabilizing agent is an anti-freeze-thaw stabilizer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5% of defoamer, 0.1 -0.5%, 0.4 -0.8% of a dispersing agent, 0.2 -0.4% of a preservative, and 0.1 -0.3% of a film-forming assistant ij, 0.5 -1% of a thickening agent and 0.3 -0.8% of a flatting agent; and preparing a flatting agent by using 0.3 -0.8% of a flatting agent

[0038] 20 -25% Of pigment and filler, 20 -25% of titanium dioxide, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5% of anti-formate powder, 3 -5%, 1 -3% of tltps, 5 -15% of extinction powder, 5 -15% of light extinction powder and 5 -15% of heavy metal

[0039] The name, the model and the manufacturer of the raw materials used in the embodiment of the invention are as follows:

[0040] The anionic pure-flavor styrene-acrylic emulsion is a pure-flavor styrene-acrylic emulsion ECO 702 of a batdoff; and the anion-type pure-flavor styrene-acrylic emulsion is an ECO 702 of the bester

[0041] The organic siloxane modified polymer emulsion is S8861 of shanghai sheno chemical technology co. ltd. and the hydrophobic property of the paint film is provided; the hydrophobic property of the paint film is provided; the hydrophobic property of the paint film is provided; the hydrophobic property of the paint film is provided;

[0042] Wherein the pH regulator is a multifunctional amino acid and an amino acid -95 of the dow chemistry; and the pH regulator is a multifunctional amine, namely, the dow chemistry;

[0043] The wetting agent is a high-efficiency environment-friendly low-foam surfactant EH -9 of dow chemistry; and the wetting agent is an efficient environment-friendly low-foam surfactant EH -9 of dow chemistry

[0044] The anti-freeze-thawing stabilizer is a high-boiling-point patent product FT -100 of the roller ground, and the boiling point of the product is larger than 400 DEG C; and the boiling point of the product is larger than 400 DEG C;

[0045] Wherein the defoaming agent is a molecular-grade defoaming agent a10 of the marine new material science and technology co. ltd. and the defoaming agent is a molecular-grade defoaming agent a10 of the marine new material science and technology co. inc.

[0046] The dispersing agent is a sodium polyacrylate salt dispersing agent P30 of which the content of french is high; and the dispersing agent is a sodium polyacrylate salt dispersing agent P30 with high content of french

[0047] And the weight ratio of the EPW to the metacarb is 1: 1; and the weight ratio of the EPW to the metacarb is 1: 1; and the weight ratio of the EPW to the metacarb is 1: 1;

[0048] And the film-forming auxiliary agent is a pure-smell film-forming assistant AF of a shanghai field margin chemical industry; and the film-forming auxiliary agent is a film-forming assistant AF of a shanghai field margin chemical industry;

[0049] The thickener is hydroxyethyl cellulose B30K in samsung chemical industry, the anionic alkali-soluble swelling thickener ASE 60 of the US pat. no. chemistry; and an anionic alkali-soluble expansion thickener ASE 60 of the US pat. no. uraphales; and

[0050] The leveling agent is a polyurethane flatting agent 2025 of french high tai; and the flatting agent is a polyurethane flatting agent 2025 of french high tai; and the flatting agent is a polyurethane flatting agent 2025 of french high

The titanium dioxide is sichuan dragon’s rutile type titanium dioxide (r 9996); and the titanium dioxide is the sichuan dragon’s rutile type titanium dioxide (r9996); and the titanium dioxide is the sichuan dragon’s rutile type titanium dioxide (r9996)

[0052] The formaldehyde-resistant powder is TK 401 of shanghai shandong chemical science and technology co. ltd. and the components are modified tourmaline powder and modified tourmaline powder, the negative ions are ionized by adsorbing water in the air, so that the formaldehyde is decomposed, and air is purified; the air is purified; the air is purified; the air is purified;

[0053] The extinction powder is a magnesium aluminum magnesium silicate ZeOleX 330 synthesized by an universal filler in the united states of the united states; the magnesium silicate aluminum zeylex 330 is synthesized by using matting powder as an universal filling material in the united states,

[0054] The heavy calcium is the CC -700 nm of the optical multiplexing building material and the heavy calcium is the CC -700 nm of the optical multiplexing building material

[0055] The thickening agent used in the embodiments of the present invention is hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose, hydroxyethyl cellulose: anionic alkali swelling thickener: polyurethane thickener: 3: 1; and the defoaming agent used is a raw material, and the defoaming agent is an anti-foaming agent: the weight ratio of the mineral oil defoaming agent to the molecular-grade defoaming agent is 1: 3

[0056] The invention relates to a manufacturing method of an interior wall water paint for a child room the method comprises the following steps: 1, preparing an interior wall water paint for a child room, comprising the following steps: 1, preparing an interior wall water paint for a child room, comprising the following steps:

[0057] The method comprises the following steps: adding four parts of deionized water into the paint mixing tank according to the formula amount, and adding four parts of deionized water into the paint mixing tank according to the formula amount, stirring at a rotating speed of 300 -600 r/min to obtain a rotating speed of 300 -600 r/min., one third of the thickening agent, the pH regulator, the wetting agent and the wetting agent are sequentially added into one third of the thickening agent, the pH regulator and the wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a mineral oil defoaming agent; and the anti-freeze-thawing stabilizer, the dispersing agent and the mineral oil defoaming agent

[0058] Step b, adjusting the high speed to 600 -1000 r/min, and adjusting the rotating speed to 600 -1000 r/min; step b, adjusting the high speed to 600 -1000 r/min, according to the formula amount, sequentially adding the titanium dioxide powder, the anti-formaldehyde powder and the titanium dioxide powder into the titanium dioxide powder and the anti-formaldehyde powder

, A matting powder and a heavy calcium; and

[0059] Step c, increase the rotation speed to 1200 r/min, and increase the rotation speed to 1200 r/min., pulping the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers; and preparing the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers;

[0060] Step d, reducing the rotating speed to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800, sequentially adding one-fifth of deionized water, a molecular-level defoaming agent and an anionic pure-flavor styrene-acrylic emulsion, organic siloxane modified polymer emulsion, coalescing agent, preservative and leveling agent, 3-thirds of the thickening agent with a viscosity of 25°c and a viscosity of 105 -110.

[0061] Embodiment 1

[0062] The invention relates to interior wall water paint for a child room. The interior wall water paint is prepared from the following raw materials in percentage by weight: emulsion: 35% anionic purified styrene-acrylic emulsion and…. 10% Organosiloxane modified polymer emulsion; the auxiliary agent is 0.05% of a pH regulator and 22.45% of deionized water, 0.1% of tltps, 0.4% of wetting agent and 0.4% of anti-freeze-thaw stabilizer, 0.3% of a defoaming agent, 0.4% of a dispersing agent, 0.2% of a preservative and 0.3% of a coalescing agent

0.5% Of a thickening agent and 0.8% of a flatting agent; and 2, a leveling agent of 0.8%

[0065] 20% Of titanium dioxide, 3% of anti-formaldehyde powder, 20% of titanium dioxide, 3% of anti-formaldehyde powder, 20% of titanium dioxide and 3% of anti-formaldehyde powder, 1.5% extinction powder and 5% calcium carbonate

[0066] The manufacturing method comprises the following steps: preparing a base material, wherein the manufacturing method comprises

[0067] The method comprises the following steps: adding four parts of deionized water into the paint mixing tank according to the formula amount, and adding four parts of deionized water into the paint mixing tank according to the formula amount, stirring at a rotating speed of 300 -600 r/min to obtain a rotating speed of 300 -600 r/min., one third of the thickening agent, the pH regulator, the wetting agent and the wetting agent are sequentially added into one third of the thickening agent, the pH regulator and the wetting agent, an anti-freeze-thaw stabilizer, a dispersing agent and a mineral oil defoaming agent; and the anti-freeze-thawing stabilizer, the dispersing agent and the mineral oil defoaming agent

[0068] Step b, adjusting the high speed to 600 -1000 r/min, and adjusting the rotating speed to 600 -1000 r/min; step b, adjusting the high speed to 600 -1000 r/min, according to the formula amount, sequentially adding the titanium dioxide powder, the anti-formaldehyde powder and the titanium dioxide powder into the titanium dioxide powder and the anti-formaldehyde powder

, A matting powder and a heavy calcium; and

[0069] Step c, increase the rotation speed to 1200 r/min, and increase the rotation speed to 1200 r/min., pulping the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers; and preparing the paint slurry for 30 minutes, wherein the fineness of the paint slurry is less than or equal to 55 micrometers;

[0070] Step d, reducing the rotating speed to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800 r/min, and according to the formula amount, the rotating speed is reduced to 600 -800, sequentially adding one-fifth of deionized water, a molecular-level defoaming agent and an anionic pure-flavor styrene-acrylic emulsion, organic siloxane modified polymer emulsion, coalescing agent, preservative and leveling agent, 3-thirds of the thickening agent with a viscosity of 25°c and a viscosity of 105 -110.

[0071] Embodiment 2

[0072] The invention relates to interior wall water paint for a child room. The interior wall water paint is calculated according to the weight percentage, the emulsion is prepared from the following raw materials in parts by weight: 25% of anionic odorless styrene-acrylic emulsion and 7% of organosiloxane modified polymer emulsion; and preparing an organic siloxane modified polymer emulsion by using a 25% anionic net-flavor styrene-acrylic emulsion and 7% of organosiloxane modified polymer emulsion

[0074] The auxiliary agent is 0.05% of a pH regulator and 29.9% of deionized water, 0.1% of a wetting agent, 0.3% of an anti-freeze-thaw stabilizer, 0.3% of an anti-freeze-thaw stabilizer, 0.3% of an anti-freeze-thaw stabilizer, 0.3% of an anti-freeze-thaw stabilizer, 0.3% of a defoamer, 0.4% of a dispersant, 0.2% of a preservative, 0.2% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a coalescing agent, 0.7% of a

5 % Of a thickening agent and 0.8% of a flatting agent

[0075] 20% Of titanium dioxide, 4% of anti-formaldehyde powder and 4% of anti-formaldehyde powder, 1% extinction powder and 10% calcium carbonate

[0076] The manufacturing method of the same is the same as that of embodiment 1

[0077] Embodiment 3

[0078] The invention relates to interior wall water paint for a child room. The interior wall water paint is calculated according to the weight percentage, the emulsion is prepared from the following raw materials in parts by weight: 50% anionic odorless styrene-acrylic emulsion and 5% of organosiloxane modified polymer emulsion; and preparing a 5% organic siloxane modified polymer emulsion

[0080] Didij: 0.1% of pH regulator and 14.1% of deionized water, 0.1% of a wetting agent, 0.1% of an anti-freeze-thaw stabilizer and 0.1% of a defoamer, 0.4% of dispersing agent, 0.2% of preservative and 0.1% of coalescing agent, 0.5% of thickening agent and 0.3% of flatting agent;

[0081] 20% Of titanium dioxide, 3% of anti-formaldehyde powder, 20% of titanium dioxide, 3% of anti-formaldehyde powder, 20% of titanium dioxide and 3% of anti-formaldehyde powder, 1% extinction powder and 5% calcium carbonate

[0082] The manufacturing method of the same is the same as that of embodiment 1

[0083] Embodiment 4

[0084] The invention relates to interior wall water paint for a child room. The interior wall water paint is calculated according to the weight percentage, the emulsion is prepared from the following raw materials in parts by weight: [ 0085 ]: 25% of anionic odorless styrene-acrylic emulsion and 5% of organosiloxane modified polymer emulsion; and preparing a 5% of organic siloxane modified polymer emulsion

[0086] The assistant is 0.05% of a pH regulator and 17.85% of deionized water, 0.2% of wetting agent, 0.5% of anti-freeze-thaw stabilizer, 0.5% of anti-freeze-thaw stabilizer, 0.5% of anti-freeze-thaw stabilizer, 0.5% of anti-freeze-thaw stabilizer, 0.5% of anti -, 0.5% of a defoaming agent, 0.8% of a dispersing agent, 0.4% of a preservative and 0.2% of a coalescing agent

0.5% Of a thickening agent and 0.3% of a flatting agent; and 2, a leveling agent of 0.3%; and 2, a leveling agent of 0.3%

[0087] 25% Of titanium dioxide, 5% of anti-formate powder, 25% of titanium dioxide, 5% of antiformate, 25% of titanium dioxide, 5% of antiformate, 25% of titanium dioxide, 5% of antiformate, 25, 3% extinction powder and 15% calcium carbonate

[0088] The manufacturing method of the same is the same as that of embodiment 1

[0089] And the detection data of the interior wall water paint for the child room are as follows:

[0090] The above embodiments are merely preferred embodiments of the present invention, general changes and substitutions made by those skilled in the art within the technical solution of the present invention are all included within the protection scope of the present invention.